A Comparative Evaluation of the Retention of Tooth Coloured and Stainless Steel Endodontic Posts: An In-vitro Study
Published: April 1, 2014 | DOI: https://doi.org/10.7860/JCDR/2014/.4220
Kiran Keswani, Rahul Maria, Rohit Punga
1. Reader, Department of Conservative Dentistry and Endodontics, Vyas Dental College and Hospital, Jodhpur, Rajasthan, India.
2. Head of the Department, Department of Conservative Dentistry and Endodontics, RishiRaj College of Dental Sciences, Bhopal, Madhya Pradesh, India.
3. Senior Lecturer, Department of Oral and Maxillofacial Surgery, Vyas Dental College and Hospital, Jodhpur, Rajasthan, India.
Correspondence
Dr. Kiran Keswani,
J - 12/62, Rajouri Garden, New Delhi-110027, India.
Phone: +919636909994, E-mail: drkirankeswani@gmail.com
Aims: This in vitro study evaluated: a) the retention of stainless steel posts of 1.5 mm diameter which were cemented with Zinc Phosphate cement versus Glass fiber posts with 1.1 mm, 1.3 mm and 1.5 mm diameters which were cemented with resin cement and b) the effect of change in diameter on the retention of Glass fiber posts with 1.1 mm, 1.3 mm and 1.5 mm diameters.
Materials and Methods: Sixty extracted mandibular premolar teeth were endodontically treated and randomly assigned to four groups of fifteen teeth each. In Groups I, II and III glass fibre posts with diameters 1.1 mm, 1.3 mm and 1.5 mm were cemented by using resin cement. In Group IV, stainless steel posts with diameter 1.5 mm were cemented by using zinc phosphate cement. The specimens were tested for tensile loading at a cross head speed of 2.0 mm/min, on a universal testing machine.
Statistical Analysis Used: One way analysis of variance and Tukey’s (post-hoc) test.
Results: Mean tensile strength from highest to lowest was in the order of Group IV, Group II, Group III, Group I. Statistically significant differences were observed between the mean tensile strengths between Groups I and II, Groups I and III, Groups I and IV, Groups II and IV, Groups III and IV, while non significant differences were observed between Groups II and III.
Conclusion: Stainless steel posts were more retentive than glass fibre posts. Glass fibre posts with 1.3mm or 1.5mm diameters provided significantly greater retention as compared to 1.1mm diameter posts.
[